مقاله A New Friction Stir Processing Method for Fabricating AZ91/SiC Nanoدرcomposite pdf دارای 6 صفحه می باشد و دارای تنظیمات در microsoft word می باشد و آماده پرینت یا چاپ است
فایل ورد مقاله A New Friction Stir Processing Method for Fabricating AZ91/SiC Nanoدرcomposite pdf کاملا فرمت بندی و تنظیم شده در استاندارد دانشگاه و مراکز دولتی می باشد.
این پروژه توسط مرکز مرکز پروژه های دانشجویی آماده و تنظیم شده است
توجه : در صورت مشاهده بهم ریختگی احتمالی در متون زیر ،دلیل ان کپی کردن این مطالب از داخل فایل ورد می باشد و در فایل اصلی مقاله A New Friction Stir Processing Method for Fabricating AZ91/SiC Nanoدرcomposite pdf ،به هیچ وجه بهم ریختگی وجود ندارد
سال انتشار: 1389
محل انتشار: دومین کنفرانس بین المللی کامپوزیت
تعداد صفحات: 6
چکیده:
In this investigation, a new method of friction stir processing (FSP) was applied to fabricate SiC/AZ91 composite layer. Current FSP methods suffer from inhomogeneous distribution of reinforcement particles in the processed area. Besides, they are unable to produce composite layer in a wide area. In this investigation, the SiC powder was packed into the grooves on AZ91 sheet perpendicular to the tool direction. The distance between the grooves centerline was 4mm and six-pass FSP with 2.5 mm overlap was carried out. Particles distribution, microstructure and hardness were evaluated on the surface and inside the processed area. Moreover, the wear characteristics of the resulted composite were evaluated using a pin-on-disc wear tester at room temperatures. It was found that the reinforcement particles were distributed uniformly inside the nugget zone and on the surface without any agglomeration taking place. The hardness and grain size of different points on the surface were almost constant. The microstructure and hardness of stirred zone (SZ) were homogeneous in longitudinal and transverse directions. The fabricated AZ91/SiC nanocomposite showed superior wear resistance to that of plain AZ91 alloy.